SrO-reinforced potassium sodium borophosphate bioactive glasses: Compositional, physical, spectral, structural properties and photon attenuation competence
No Thumbnail Available
Files
Date
2021
Journal Title
Journal ISSN
Volume Title
Publisher
ELSEVIER
Abstract
The melt quenching process is assumed in making the glass system 45P2O5-15B2O3-22Na2O-(18-x) K2O: xSrO
where x =0-12 mol%, namely as S1-S5. Compositional, physical, spectral, structural properties and radiations
attenuation competences of S1-S5 bioglasses have been investigated compared to ordinary concrete (OC) cortical
bone (CB) and soft tissue (ST). The density of the prepared bioactive glasses has been found to increase with an
increase in the SrO content, whereas an opposite trend has been observed in the molar volume. FTIR study shows
the existence of different structural groups such as BO3, BO4 and BPO4 units in the network. Optical absorption
spectra of the glasses revealed that the cutoff wavelength decreases with increased in SrO content. The maximum
(minimum) MAC values were 7.986 (0.021), 7.925 (0.0214), 7.863 (0.0217), 7.865 (0.0217) and 8.837 (0.022)
cm2/g for S1, S2, S3, S4, and S5, respectively. The maximum value of LAC was also obtained at 15 keV with
values equal to: 18.528, 18.942, 19.343, 19.898, and 20.144 cm1 respectively for S1-S5. At 0.1, 1.0, and 10
MeV, values of HVT of the glasses were 1.72, 1.54, 1.38, 1.34, and 1.14 cm for S1-S5, respectively, however, the
HVT of S1–S5 were less than that of ordinary concrete (OC). The MFP was reduced as SrO content of the S1-S5
glasses increased. Results of the calculated radiation interaction parameters showed that S5 is a better photon,
proton and electron absorber compared to the other four bioactive glasses in this study. Improving in photon
absorption of the glasses was recorded for higher SrO content. The effect of SrO addition on photon (energy)
absorption is more significant for photon energies less than 0.2 MeV. The studied bioactive glasses can function
better than ordinary concrete for photon shielding applications.