School of Infrastructure Process Engineering and Technology (SIPET)
Permanent URI for this communityhttp://197.211.34.35:4000/handle/123456789/27
School of Infrastructure Process Engineering and Technology (SIPET)
Browse
2 results
Search Results
Item Statistical Model for Predicting Slump and Strength of Concrete Containing Date Seeds(Covenant Journal of Engineering Technology (CJET), 2021-06-10) YUSUF, Abdulazeez; Jamal, J. O.; Abubakar, M.; Aminulai, H. O.Incorporating agro-based waste in concrete can reduce environmental pollution and lead to preserving the ecosystem. In order to reduce trial and error in achieving desired slump and compressive strength of concrete containing Date Seed (DS), this paper examines the slump and compressive strength of concrete using date seeds as a partial replacement for crushed granite. Preliminary tests were conducted on the aggregates to ascertain their suitability for concrete production. Concrete with DS-crushed granite ratios of 0:100, 5:95, 10:90, 15:85, and 20:80 were prepared using a mix ratio of 1:2:4 and a water-cement ratio of 0.5. Slump loss was used to estimate the workability of the fresh concrete. The freshly prepared concrete was cast in 150 x 150 x 150 mm and the compressive strength was determined after curing by full immersion in water for 7, 14, 21 and 28 days. Results showed that the slump of concrete increased with an increase in the content of date seed. The compressive strength was inversely proportional to the date seed content with a DS crushed granite ratio of 20:80 recording the lowest compressive strength (20N/mm2). Linear regression models for slump and compressive strength were developed and found to be sufficient in explaining the experimental data based on a Mean Square Error (MSE) of 0.37 and 0.029 and R2 of 88% and 99% obtained for slump and compressive strength respectively. The study has concluded that DS can be used as a partial replacement for crushed granite in concrete and a linear model is sufficient in predicting the slump and strength of concrete containing date seeds.Item Dimensional Compliance and Compressive Strength of Sandcrete Hollow Blocks Produced in Minna Metropolis(International Engineering Conference (IEC 2017) Federal University of Technology, Minna, Nigeria, 2017) Yusuf, Abdulazeez; Aminulai, H.O.; Abdullahi, A; Alhaji, B; Alalade, A.I.The study was carried out to investigate the level of dimensional compliance of commercially produced sandcrete blocks in Minna metropolis and also determine the compressive strength of collected block samples. One hundred and sixty (160), nine (9) inch hollow sandcrete block samples were collected from ten sandcrete block producing companies. Fine aggregate samples were collected from the hollow sandcrete block companies along with the hollow sandcrete blocks. Sieve analysis was carried out on the soil samples. Density, water absorption and dimension of the collected Sandcrete block samples were determined. Compressive strength at 7 and 14 days curing age was also determined. Results indicate that the fine aggregates used were not suitable for block making as the coefficient of uniformity of soil samples range from 0.71 – 1.89 while the coefficient of curvature lie within 2.57 to 4.80 which do not conform to standard. None of the Sandcrete block production company met the required standard dimension as specified by Nigeria Industrial standard (NIS). Test results also revealed that the water abortion capacity of all collected block samples were below 12% maximum recommended by NIS except for block industry M which recorded 12.08%. The density was between 1.59 g/cm3 – 5.05 g/cm3, greater than 1.5g/cm3 specified by NIS. The average compressive strength was between 0.21N/mm2 - 1.11N/mm2 at 14 days curing age which was less than 3.45 N/mm2 specified by NIS. It was recommended that block producing industries should be enforced by the standard organization of Nigeria to follow the recommended standard dimensions by carrying out routine check.